上海隆进特殊钢有限公司

安庆gx40nicrsi3525对应牌号、gx40nicrsi3525、gx40nicrsi3525、gx40nicrsi3525

上海隆进特殊钢有限公司提供图片

s-nimo16cr16w s-nimo15cr15w nicr20ti nicr20tial nife25cr20nbti x7crnico212020 g-x15crnico212020 x40crniconb1313 cocr20w15ni cocr20w15ni gx7crninb1613 nicr20co18ti x12crconi2120 nicr19como nifecr12mo nicr20mo x40cocrni2020 x50cocrni2020 cocr28moni x5nicrti2615 x8crnimonb1616 nicr20cbmo nicr18co cocr20ni20w

k211 k213 k214 k401 k402 k403 k405 k406 k406c k407 k408 k409 k412 k417 k417g k417l k418 k418b k419 k419h k11 k13 k14 k1 k2 k3 k5 k6 k6c k7 k8 k9 k12 k17 k17g k17l k18 k18b k19 k19h k423 k423a k424 k430 k438 k438g k441 k461 k477 k480 k491 k4002 k4130 k4163
k4169 k4202 k4242 k4536 k4537 k4648 k4708 k23 k23a k26 k430 k38 k38g k41 k461 k77 k80 k91 k002 k130 k163 k4169 k202 k242 k536 k537 k648 k708 k605 k610 k612 k640 k640m k6188 k825 k605 k10 k612 k40 k40m k188 k25 dz404 dz405 dz417g dz422 dz422b dz438g dz4002 dz4125 dz4125l dz640m dz4 dz5 dz17g dz22 dz22b dz38g dz002 dz125 dz125l

生产工艺：
冶炼方面：为了更纯净化的钢水，减低气体含量与有害元素含量；同时由于部分合金中有易氧化元素如al，ti等存在，非真空冶裂以控制；更是为了的热塑性，镍基耐热合金，通常采用真空感应炉熔炼，甚至用真空感应冶炼加真空自耗炉或电渣炉重熔进行生产。
变形方面：采用锻造、轧制工艺，对于热塑性差的合金甚至采用开坯后轧制或用软钢(或不锈钢)包套直接工艺。变形的目的是为了破碎铸造组织，微观组织结构。
铸造方面：通常用真空感应炉熔粮合金成分与控制气体与杂质含量，并用真空重熔-精密铸造法制成零件。
热处理方面：变形合金和部分铸造合金需进行热处理，包括固溶处理、中间处理和时效处理，以udmet 500合金为例，它的热处理制度分为四段：固溶处理，1175℃，2小时，空冷；中间处理，1080℃，4小时，空冷；一次时效处理，843℃，24小时，空冷；二次时效处理，760℃，16小时，空冷。以所要求的组织状态和的综合性能。

上海隆进特殊钢有限公司提供资料